Microstructural Deterioration Mechanism of Directionally Solidified Ni-Based Superalloy Used in First-Stage Industrial Gas Turbine Blades after Ultra Long-Term Service
Materials Characterization（2024）
关键词
Turbine blades,Microstructural deterioration,gamma' precipitates,Coating,Interface,Failure modes